CoCrMo-base Alloys for Dental Applications Obtained by Selective laser melting (SLM) and CAD/CAM Milling (2020)

• Authors:
  • SANTOS, Claudinei dos
  • HABIBE, Alexandre Fernandes
  • SIMBA, BRUNO GALVÃO
  • Lins, Jefferson Fabrício Cardoso
  • FREITAS, BRUNO XAVIER DE
  • Nunes, Carlos Angelo
• USP affiliated authors: NUNES, CARLOS ANGELO - EEL ; FREITAS, BRUNO XAVIER DE - EEL
• Unidade: EEL
• DOI: 10.1590/1980-5373-MR-2019-05999
• Assunto: LIGAS DENTÁRIAS
• Keywords: Caracterização Microestrutural; Propriedades Mecânicas; Fabricação de aditivos
• Agências de fomento:
  • Financiamento FAPERJ
  • Financiamento FINEP
  • Financiamento CAPES
• Language: Inglês
• Abstract: In this work, CoCrMo-base alloys specimens were produced by additive manufacturing using selective laser melting (SLM) as well as CAD/CAM milling. For SLM specimens, spherical particles were laser processed at 1320°C under argon atmosphere and submitted to thermal stress relieving at 750°C–45min. Specimens from CoCrMo blocks were milled by CAD/CAM machining and sintered at 1300°C–60min. The materials from both techniques were characterized by relative density, dilatometry, SEM/BSE, OM and XRD analysis. The mechanical properties were determined by Vickers hardness and tensile tests. The specimens from both techniques exhibited single phase γCo (FCC) and CTE of 14 x10-6 °C-1. Relative density of 95.4%/ 85.6%, hardness values near 400HV/ 350HV and UTS of 905MPa/ 780MPa were measured for SLM and CAD/CAM specimens, respectively. Higher relative density is the main factor for increased mechanical properties of SLM specimens. On the other hand, both SLM and CAD/CAM specimens present properties in accordance with ISO-22674 recommendations, compatible with dental applications such as bridges containing four or more elements as well as fully dense pontics.
• Source:
  • Título: Materials research
  • ISSN: 19805373
  • Volume/Número/Paginação/Ano: v23., n2. , p.1-6, 2020

Informações sobre o DOI: 10.1590/1980-5373-MR-2019-05999 (Fonte: oaDOI API)
• Este periódico é de acesso aberto
• Este artigo NÃO é de acesso aberto
  

---

How to cite

A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas

• ABNT

  SANTOS, Claudinei dos et al. CoCrMo-base Alloys for Dental Applications Obtained by Selective laser melting (SLM) and CAD/CAM Milling. Materials research, p. 1-6, 2020Tradução . . Disponível em: https://doi.org/10.1590/1980-5373-MR-2019-05999. Acesso em: 30 dez. 2025.

• APA

  SANTOS, C. dos, HABIBE, A. F., SIMBA, B. R. U. N. O. G. A. L. V. Ã. O., Lins, J. F. C., FREITAS, B. R. U. N. O. X. A. V. I. E. R. D. E., & Nunes, C. A. (2020). CoCrMo-base Alloys for Dental Applications Obtained by Selective laser melting (SLM) and CAD/CAM Milling. Materials research, 1-6. doi:10.1590/1980-5373-MR-2019-05999

• NLM

  SANTOS C dos, HABIBE AF, SIMBA BRUNOGALVÃO, Lins JFC, FREITAS BRUNOXAVIERDE, Nunes CA. CoCrMo-base Alloys for Dental Applications Obtained by Selective laser melting (SLM) and CAD/CAM Milling [Internet]. Materials research. 2020 ; 1-6.[citado 2025 dez. 30 ] Available from: https://doi.org/10.1590/1980-5373-MR-2019-05999

• Vancouver

  SANTOS C dos, HABIBE AF, SIMBA BRUNOGALVÃO, Lins JFC, FREITAS BRUNOXAVIERDE, Nunes CA. CoCrMo-base Alloys for Dental Applications Obtained by Selective laser melting (SLM) and CAD/CAM Milling [Internet]. Materials research. 2020 ; 1-6.[citado 2025 dez. 30 ] Available from: https://doi.org/10.1590/1980-5373-MR-2019-05999

Últimas obras dos mesmos autores vinculados com a USP cadastradas na BDPI:

• Sintering behaviour of Co-28%Cr-6%Mo compacted blocks for dental prosthesis
• Mechanical Alloying and Hot Pressing of Ti-Zr-Si-B Powder Mixtures
• Caracterização de blocos sinterizados à base de CoCrMo visando a obtenção de próteses odontológicas por fresagem CAD/CAM
• Reduction of Magnesium Corrosion Rate by PMMA-co-PMAA Films
• Effect of hot swaging on microstructure and properties of aged Ti-10Mo-20Nb alloy
• Effect of zirconium addition on the phase transformations in as-cast and heat-treated Ti–Zr–Si–B alloys
• Creep Properties of Directionally Solidified Nb-Modified Ni-Base Superalloy, Mar-M247
• Thermodynamic assessment of the RE-Zn (RE = Dy, Er, Ho, Tb) binaries as a starting step for a Mg-Zn-Zr-Rare earth multicomponent database
• Microstructural and Mechanical Characterization of Directionally Solidified Conventional and Nb-Modified Mar-M247 Superalloy
• Microstructure and corrosion behavior in SBF medium of spark plasma sintered Ti-xZr-20Si-10B (x = 5, 7, 10, 15, 20-at.-%) alloys