Stress corrosion cracking and corrosion fatigue analysis of API X70 steel exposed to a circulating ethanol environment (2022)

• Authors:
  • Santos, Elielson Alves dos
  • Giorgetti, Vinicius
  • Souza Junior, Celso A. de
  • Marcomini, José Benedito
  • Sordi, Vitor Luiz
  • Rovere, Carlos Alberto Della
• Autor USP: MARCOMINI, JOSÉ BENEDITO - EESC
• Unidade: EESC
• DOI: 10.1016/j.ijpvp.2022.104846
• Subjects: FADIGA DOS MATERIAIS; CORROSÃO DOS MATERIAIS; ETANOL; MATERIAIS
• Agências de fomento:
  • Financiado pelo CNPq
  • Financiado pela CAPES
• Language: Inglês
• Imprenta:
  • Publisher: Elsevier
  • Publisher place: London
  • Date published: 2022
• Source:
  • Título: International Journal of Pressure Vessels and Piping
  • ISSN: 0308-0161
  • Volume/Número/Paginação/Ano: v. 200, article 104846, p. 1-12, 2022


Informações sobre a disponibilidade de versões do artigo em acesso aberto coletadas automaticamente via oaDOI API (Unpaywall).

Status:

Artigo possui versão em acesso aberto em repositório (Green Open Access)

Versão do Documento:

Versão publicada (Published version)

Acessar versão aberta:

• URL de acesso aberto
• PDF de acesso aberto

Por se tratar de integração com serviço externo, podem existir diferentes versões do trabalho (como preprints ou postprints), que podem diferir da versão publicada.

---

Download do texto completo

Tipo	Nome	Link
	1-s2.0-S0308016122002319-...

How to cite

A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas

• ABNT

  SANTOS, Elielson Alves dos et al. Stress corrosion cracking and corrosion fatigue analysis of API X70 steel exposed to a circulating ethanol environment. International Journal of Pressure Vessels and Piping, v. 200, p. 1-12, 2022Tradução . . Disponível em: https://doi.org/10.1016/j.ijpvp.2022.104846. Acesso em: 02 abr. 2026.

• APA

  Santos, E. A. dos, Giorgetti, V., Souza Junior, C. A. de, Marcomini, J. B., Sordi, V. L., & Rovere, C. A. D. (2022). Stress corrosion cracking and corrosion fatigue analysis of API X70 steel exposed to a circulating ethanol environment. International Journal of Pressure Vessels and Piping, 200, 1-12. doi:10.1016/j.ijpvp.2022.104846

• NLM

  Santos EA dos, Giorgetti V, Souza Junior CA de, Marcomini JB, Sordi VL, Rovere CAD. Stress corrosion cracking and corrosion fatigue analysis of API X70 steel exposed to a circulating ethanol environment [Internet]. International Journal of Pressure Vessels and Piping. 2022 ; 200 1-12.[citado 2026 abr. 02 ] Available from: https://doi.org/10.1016/j.ijpvp.2022.104846

• Vancouver

  Santos EA dos, Giorgetti V, Souza Junior CA de, Marcomini JB, Sordi VL, Rovere CAD. Stress corrosion cracking and corrosion fatigue analysis of API X70 steel exposed to a circulating ethanol environment [Internet]. International Journal of Pressure Vessels and Piping. 2022 ; 200 1-12.[citado 2026 abr. 02 ] Available from: https://doi.org/10.1016/j.ijpvp.2022.104846

Últimas obras dos mesmos autores vinculados com a USP cadastradas na BDPI:

• Influência do etanol sobre o comportamento em fadiga do aço API 5L X70
• Stress corrosion cracking and fatigue crack growth of an API 5L X70 welded joint in an ethanol environment
• Caracterização da nova liga Fe-C-Mn-Si-Cr: fragilização da martensita revenida e curvas de revenimento
• Characterization of a New Fe-C-Mn-Si-Cr Bearing Alloy: Tempered Martensite Embrittlement Susceptibility
• Investigation of a fatigue failure in a stainless steel femoral plate
• Fatigue crack propagation of API 5L X70 steel in a modifed simulated fuel-grade ethanol (MSFGE) environment
• Failure analysis of a hot forged SAE 4140 steel kingpin
• Corrosion Behavior and Microstructural Characterization of Friction Stir Welded API X70 Steel