Stress corrosion cracking and fatigue crack growth of an API 5L X70 welded joint in an ethanol environment (2019)
- Authors:
- Autor USP: MARCOMINI, JOSÉ BENEDITO - EESC
- Unidade: EESC
- DOI: 10.1016/j.ijpvp.2019.01.006
- Subjects: CORROSÃO; FADIGA DOS MATERIAIS; AÇO CARBONO
- Agências de fomento:
- Language: Inglês
- Imprenta:
- Source:
- Título: International Journal of Pressure Vessels and Piping
- ISSN: 0308-0161
- Volume/Número/Paginação/Ano: v. 169, p. 223-229, jan. 2019
- Este periódico é de assinatura
- Este artigo NÃO é de acesso aberto
- Cor do Acesso Aberto: closed
-
ABNT
GIORGETTI, Vinicius et al. Stress corrosion cracking and fatigue crack growth of an API 5L X70 welded joint in an ethanol environment. International Journal of Pressure Vessels and Piping, v. 169, n. ja 2019, p. 223-229, 2019Tradução . . Disponível em: https://doi.org/10.1016/j.ijpvp.2019.01.006. Acesso em: 04 out. 2024. -
APA
Giorgetti, V., Santos, E. A. dos, Marcomini, J. B., & Sordi, V. L. (2019). Stress corrosion cracking and fatigue crack growth of an API 5L X70 welded joint in an ethanol environment. International Journal of Pressure Vessels and Piping, 169( ja 2019), 223-229. doi:10.1016/j.ijpvp.2019.01.006 -
NLM
Giorgetti V, Santos EA dos, Marcomini JB, Sordi VL. Stress corrosion cracking and fatigue crack growth of an API 5L X70 welded joint in an ethanol environment [Internet]. International Journal of Pressure Vessels and Piping. 2019 ; 169( ja 2019): 223-229.[citado 2024 out. 04 ] Available from: https://doi.org/10.1016/j.ijpvp.2019.01.006 -
Vancouver
Giorgetti V, Santos EA dos, Marcomini JB, Sordi VL. Stress corrosion cracking and fatigue crack growth of an API 5L X70 welded joint in an ethanol environment [Internet]. International Journal of Pressure Vessels and Piping. 2019 ; 169( ja 2019): 223-229.[citado 2024 out. 04 ] Available from: https://doi.org/10.1016/j.ijpvp.2019.01.006 - Caracterização da nova liga Fe-C-Mn-Si-Cr: fragilização da martensita revenida e curvas de revenimento
- Stress corrosion cracking and corrosion fatigue analysis of API X70 steel exposed to a circulating ethanol environment
- Influência do etanol sobre o comportamento em fadiga do aço API 5L X70
- Characterization of a New Fe-C-Mn-Si-Cr Bearing Alloy: Tempered Martensite Embrittlement Susceptibility
- Investigation of a fatigue failure in a stainless steel femoral plate
- Failure analysis of a hot forged SAE 4140 steel kingpin
- Fatigue crack propagation of API 5L X70 steel in a modifed simulated fuel-grade ethanol (MSFGE) environment
- Corrosion Behavior and Microstructural Characterization of Friction Stir Welded API X70 Steel
Informações sobre o DOI: 10.1016/j.ijpvp.2019.01.006 (Fonte: oaDOI API)
Download do texto completo
| Tipo | Nome | Link | |
|---|---|---|---|
 | prod_022886_sysno_3005387... |
How to cite
A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas