Role of microstructure and crystallographic orientation in fatigue crack failure analysis of a heavy haul railway rail (2019)
- Authors:
- USP affiliated authors: GOLDENSTEIN, HELIO - EP ; SINATORA, AMILTON - EP ; MASOUMI, MOHAMMAD - EP
- Unidade: EP
- DOI: 10.1016/j.engfailanal.2018.10.022
- Subjects: CRISTALOGRAFIA; FADIGA DAS ESTRUTURAS; TRILHOS
- Language: Inglês
- Imprenta:
- Source:
- Título: Engineering Failure Analysis
- ISSN: 1350-6307
- Volume/Número/Paginação/Ano: v.96, p. 320-329, 2019
- Status:
- Nenhuma versão em acesso aberto identificada
-
ABNT
MASOUMI, Mohammad e SINATORA, Amilton e GOLDENSTEIN, Hélio. Role of microstructure and crystallographic orientation in fatigue crack failure analysis of a heavy haul railway rail. Engineering Failure Analysis, v. 96, p. 320-329, 2019Tradução . . Disponível em: https://doi.org/10.1016/j.engfailanal.2018.10.022. Acesso em: 09 maio 2026. -
APA
Masoumi, M., Sinatora, A., & Goldenstein, H. (2019). Role of microstructure and crystallographic orientation in fatigue crack failure analysis of a heavy haul railway rail. Engineering Failure Analysis, 96, 320-329. doi:10.1016/j.engfailanal.2018.10.022 -
NLM
Masoumi M, Sinatora A, Goldenstein H. Role of microstructure and crystallographic orientation in fatigue crack failure analysis of a heavy haul railway rail [Internet]. Engineering Failure Analysis. 2019 ;96 320-329.[citado 2026 maio 09 ] Available from: https://doi.org/10.1016/j.engfailanal.2018.10.022 -
Vancouver
Masoumi M, Sinatora A, Goldenstein H. Role of microstructure and crystallographic orientation in fatigue crack failure analysis of a heavy haul railway rail [Internet]. Engineering Failure Analysis. 2019 ;96 320-329.[citado 2026 maio 09 ] Available from: https://doi.org/10.1016/j.engfailanal.2018.10.022 - Microstructure and crystallographic orientation evolutions below the superficial white layer of a used pearlitic rail
- Role of crystallographic orientation and grain boundaries in fatigue crack propagation in used pearlitic rail steel
- Influência da adição de nióbio e molibdênio na decomposição isotérmica da austenita em aço 0,7 % C
- Non classical eutectoid decomposition products morphologies in Fe-Cr-C and Fe-Cr-Mo-C steels
- Efeito da morfologia e do numero de particulas de grafita na fratura de ferros fundidos com matriz ferritica
- Introducao a metalurgia dos ferros fundidos brancos com alto cromo
- Improvement in the wear resistance of a hypereutectoid rail via heat treatment
- Teores de carbono, cromo e molibdênio
- Efeito da morfologia e do numero de particulas de grafita na fratura de ferros fundidos com matriz ferritica
- Ferros fundidos brancos de alto cromo: resistencia ao impacto
Informações sobre a disponibilidade de versões do artigo em acesso aberto coletadas automaticamente via oaDOI API (Unpaywall).
Download do texto completo
| Tipo | Nome | Link | |
|---|---|---|---|
 |
Sinatora-2019-Role of mic... |
How to cite
A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas