Role of microstructure and crystallographic orientation in fatigue crack failure analysis of a heavy haul railway rail (2019)
- Autores:
- Autores USP: GOLDENSTEIN, HELIO - EP ; SINATORA, AMILTON - EP ; MASOUMI, MOHAMMAD - EP
- Unidade: EP
- DOI: 10.1016/j.engfailanal.2018.10.022
- Assuntos: CRISTALOGRAFIA; FADIGA DAS ESTRUTURAS; TRILHOS
- Idioma: Inglês
- Imprenta:
- Fonte:
- Título do periódico: Engineering Failure Analysis
- ISSN: 1350-6307
- Volume/Número/Paginação/Ano: v.96, p. 320-329, 2019
- Este periódico é de assinatura
- Este artigo NÃO é de acesso aberto
- Cor do Acesso Aberto: closed
-
ABNT
MASOUMI, Mohammad e SINATORA, Amilton e GOLDENSTEIN, Hélio. Role of microstructure and crystallographic orientation in fatigue crack failure analysis of a heavy haul railway rail. Engineering Failure Analysis, v. 96, p. 320-329, 2019Tradução . . Disponível em: https://doi.org/10.1016/j.engfailanal.2018.10.022. Acesso em: 19 set. 2024. -
APA
Masoumi, M., Sinatora, A., & Goldenstein, H. (2019). Role of microstructure and crystallographic orientation in fatigue crack failure analysis of a heavy haul railway rail. Engineering Failure Analysis, 96, 320-329. doi:10.1016/j.engfailanal.2018.10.022 -
NLM
Masoumi M, Sinatora A, Goldenstein H. Role of microstructure and crystallographic orientation in fatigue crack failure analysis of a heavy haul railway rail [Internet]. Engineering Failure Analysis. 2019 ;96 320-329.[citado 2024 set. 19 ] Available from: https://doi.org/10.1016/j.engfailanal.2018.10.022 -
Vancouver
Masoumi M, Sinatora A, Goldenstein H. Role of microstructure and crystallographic orientation in fatigue crack failure analysis of a heavy haul railway rail [Internet]. Engineering Failure Analysis. 2019 ;96 320-329.[citado 2024 set. 19 ] Available from: https://doi.org/10.1016/j.engfailanal.2018.10.022 - Microstructure and crystallographic orientation evolutions below the superficial white layer of a used pearlitic rail
- Role of crystallographic orientation and grain boundaries in fatigue crack propagation in used pearlitic rail steel
- Ferros fundidos brancos de alto cromo: resistencia ao impacto
- Efeito do carbono, cromo e molibdenio na solidificacao e microestrutura de ferros fundidos brancos com 15 ou 20% de cromo
- Improvement in the wear resistance of a hypereutectoid rail via heat treatment
- Introducao a metalurgia dos ferros fundidos brancos com alto cromo
- Non classical eutectoid decomposition products morphologies in Fe-Cr-C and Fe-Cr-Mo-C steels
- Microestrutura dos fofo brancos de alto cromo
- Sequencia de solidificacao e metalografia quantitativa de ferros fundidos brancos com 15% de cromo
- Efeito da morfologia e do numero de particulas de grafita na fratura de ferros fundidos com matriz ferritica
Informações sobre o DOI: 10.1016/j.engfailanal.2018.10.022 (Fonte: oaDOI API)
Download do texto completo
| Tipo | Nome | Link | |
|---|---|---|---|
 | Sinatora-2019-Role of mic... |
Como citar
A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas