Artigo de periodico

Sub case origin fatigue in teeth of helical gear of a TA 67n turbo reducer (2020)

• Authors:
  • Ruchert, Cassius Olívio Figueiredo Terra
  • Maciel, Carla Isabel dos Santos
  • Chemin, Aline Emanuelle Albuquerque
• Autor USP: RUCHERT, CASSIUS OLIVIO FIGUEIREDO TERRA - EEL
• Unidade: EEL
• DOI: 10.1016/j.engfailanal.2019.104286
• Assunto: FADIGA DOS MATERIAIS
• Keywords: Turbo reducer; Gear failure; Sub case origin fatigue; Contact fatigue; Case crushing
• Language: Inglês
• Abstract: The main aim of this study is investigating the possible failures classified as subcase origin fatigue and further case crushing. Because of these failure mechanisms, the teeth of the intermediate gears shaft may fracture after several cycles of operation of the whole gearbox. Shafts are used to machines which need to transmit rotary motion into a system of parts, such as roller bearings, gears, and pulleys. In this work, a helical gear manufactured with DIN 18CrNiMo7-6 steel is an integral part of a turbo reducer, had several teeth fractured after three months of operation. The teeth were heat treated as follow: carburizing, quenching, tempering following by grinding with grinding wheels resulting in a surface hardness of the teeth between 58 and 62 HRC. The analysis of failure surface shown a bright area between the lath martensite, which is retined austenite, that decreases the contact fatigue strength. The plastic deformation transforms the retained austenite to untempered martensite, promoting the weakening of the hardened layer. The performance of composition analysis, macromolecular, optical microscopy, microhardness, and scanning electron microscopy, makes possible identifying that the crack nucleates close to the pitting corrosion line between the flank and the working face of the gear tooth. Cracks nucleated preferentially in the sublayer and propagated because of the contact fatigue, usually, pull out the upper part of the tooth entirely, which results in static propagation by the case crushing mechanism.
• Imprenta:
  • Publisher: Elsevier
  • Publisher place: São Paulo-SP
  • Date published: 2020
• Source:
  • Título: Engineering failure analysis
  • ISSN: 1350-6307
  • Volume/Número/Paginação/Ano: v. 108, p. 1-17, 2020


Informações sobre a disponibilidade de versões do artigo em acesso aberto coletadas automaticamente via oaDOI API (Unpaywall).

Status:

Nenhuma versão em acesso aberto identificada

---

How to cite

A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas

• ABNT

  RUCHERT, Cassius Olívio Figueiredo Terra e MACIEL, Carla Isabel dos Santos e CHEMIN, Aline Emanuelle Albuquerque. Sub case origin fatigue in teeth of helical gear of a TA 67n turbo reducer. Engineering failure analysis, v. 108, p. 1-17, 2020Tradução . . Disponível em: https://doi.org/10.1016/j.engfailanal.2019.104286. Acesso em: 09 abr. 2026.

• APA

  Ruchert, C. O. F. T., Maciel, C. I. dos S., & Chemin, A. E. A. (2020). Sub case origin fatigue in teeth of helical gear of a TA 67n turbo reducer. Engineering failure analysis, 108, 1-17. doi:10.1016/j.engfailanal.2019.104286

• NLM

  Ruchert COFT, Maciel CI dos S, Chemin AEA. Sub case origin fatigue in teeth of helical gear of a TA 67n turbo reducer [Internet]. Engineering failure analysis. 2020 ; 108 1-17.[citado 2026 abr. 09 ] Available from: https://doi.org/10.1016/j.engfailanal.2019.104286

• Vancouver

  Ruchert COFT, Maciel CI dos S, Chemin AEA. Sub case origin fatigue in teeth of helical gear of a TA 67n turbo reducer [Internet]. Engineering failure analysis. 2020 ; 108 1-17.[citado 2026 abr. 09 ] Available from: https://doi.org/10.1016/j.engfailanal.2019.104286

Últimas obras dos mesmos autores vinculados com a USP cadastradas na BDPI:

• Microstructural characterization and mechanical behavior at high temperature of the cast stainless steel G-NiCr28W-MA in the as cast and as welded conditions
• Simulation of retardation caused by peak loading in aircraft-grade aluminum alloy SAE-AMS 7475-T7351
• Fracture toughness evaluation of friction stir welded API 5L X-80 steel plates
• Estudo de trinca gerada no processo de dobramento a frio de grampo para feixes de mola
• Influência dos parâmetros de soldagem nas propriedades mecânicas do aço ferrítico ligado ao cromo unido por soldagem
• Fretting Fatigue In-service Failure of X20CrMo13 Stainless Steel Turbine Blade
• Fatigue crack propagation in aluminum alloy 2050: numerical analysis of acceleration and retardation
• Modelamento do fechamento da trinca por fadiga em carregamento de amplitude variável via método dos elementos finitos
• Fatigue crack growth behavior and fatigue limit determination using the staircase method for ultra high strength 300M steel
• Caracterização microestrutural da liga SAE AMS 7475 T7351