Incorporation of mold flux waste in red ceramic. (2019)
- Authors:
- USP affiliated authors: VERNILLI JUNIOR, FERNANDO - EEL ; CRISTANTE NETO, ÂNGELO - EEL
- Unidade: EEL
- DOI: 10.1016/j.jmrt.2019.09.038
- Subjects: CERÂMICA VERMELHA; ARGILAS
- Keywords: Incorporation; Mold flux; Waste
- Language: Inglês
- Abstract: This work has as its objective to evaluate the effect of mold flux waste incorporation in a red ceramic body. The mold flux waste came from an industry of additives for continuous casting of steel, in the municipal area of Guaratinguetá, State of São Paulo, Brazil. Initially, the mold flux waste was characterized in terms of chemical composition, particles size distribution, X-ray diffraction, specific surface area and scanning electron microscopy. Clay mixtures were prepared with additions of 0, 5, 10 and 20 wt.% of mold flux waste. Red ceramic specimens were produced by extrusion and then fired in an industrial furnace at 750, 850, 950 and 1050 ºC. Some physical and mechanical properties were evaluated. The results indicated that mold flux waste addition optimized the plasticity of the clayey body, increased the flexural and compressive strength and reduced the values for water absorption. The specimens with 5 wt.% of mold flux waste, at 1050 ºC firing temperature, presented the best results for the properties evaluated, indicating a higher packing for this composition. The incorporation of mold flux waste allowed improvements in the clayey body, producing better quality materials and being an appropriate way of disposal.
- Imprenta:
- Source:
- Título: Journal of Materials Research and Technology-JMR&T
- ISSN: 22387854
- Volume/Número/Paginação/Ano: v.8, n.6, p.5707-5715, 2019
- Este periódico é de acesso aberto
- Este artigo é de acesso aberto
- URL de acesso aberto
- Cor do Acesso Aberto: gold
- Licença: cc-by-nc-nd
-
ABNT
VIGNERON, Thaís Queiroz Gomes et al. Incorporation of mold flux waste in red ceramic. Journal of Materials Research and Technology-JMR&T, v. 8, n. 6, p. 5707-5715, 2019Tradução . . Disponível em: https://doi.org/10.1016/j.jmrt.2019.09.038. Acesso em: 09 out. 2024. -
APA
Vigneron, T. Q. G., Vieira, C. M. F., Delaqua, G. C. G., Vernilli Junior, F., & Cristante Neto, Â. (2019). Incorporation of mold flux waste in red ceramic. Journal of Materials Research and Technology-JMR&T, 8( 6), 5707-5715. doi:10.1016/j.jmrt.2019.09.038 -
NLM
Vigneron TQG, Vieira CMF, Delaqua GCG, Vernilli Junior F, Cristante Neto Â. Incorporation of mold flux waste in red ceramic. [Internet]. Journal of Materials Research and Technology-JMR&T. 2019 ;8( 6): 5707-5715.[citado 2024 out. 09 ] Available from: https://doi.org/10.1016/j.jmrt.2019.09.038 -
Vancouver
Vigneron TQG, Vieira CMF, Delaqua GCG, Vernilli Junior F, Cristante Neto Â. Incorporation of mold flux waste in red ceramic. [Internet]. Journal of Materials Research and Technology-JMR&T. 2019 ;8( 6): 5707-5715.[citado 2024 out. 09 ] Available from: https://doi.org/10.1016/j.jmrt.2019.09.038 - Estudo comparativo da resistência ao dano por choque térmico em refratários para conjunto de porta ventos de alto-forno
- The recycling effect of BOF slag in the portland cement properties
- Application of Glass Waste on Red Ceramic to Improve Sintering
- Reuse of wastes from the production of electrofused alumina in red ceramics
- Reducing environmental impacts: The use of basic oxygen furnace slag in portland cement
- Blast Furnace Hearth Lining: Post Mortem Analysis
- Combined Transient 3d Simulation and Experimental Methods to Evaluate a Slow Heat-Up Curve Used to Dry a Refractory Concrete
- Obtainment of the alumina polyamide-coated spherical particles
- Cimento ecossustentável sem clínquer à base de resíduos da siderurgia e da construção civil e uso do mesmo
- Binary Mixtures of ZnO/TiO2 for Solar Heterogeneous Photocatalysis of Non-Purgeable Organic Carbon in Landfill Leachate
Informações sobre o DOI: 10.1016/j.jmrt.2019.09.038 (Fonte: oaDOI API)
How to cite
A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas