Effect of surface finishing and thickness on the translucency of zirconia dental ceramis (2020)

• Authors:
  • SANTOS, Claudinei dos
  • Rosa, Gabriel Oliveira
  • Quintino, Manara Nogueira
  • Alves, M. F. R. P.
  • RIBEIRO, Sebastião
  • Silva, Claudio Luis Melo
• USP affiliated authors: RIBEIRO, SEBASTIAO - EEL ; ALVES, MANUEL FELLIPE RODRIGUES PAIS - EEL
• Unidade: EEL
• DOI: 10.1016/j.ceramint.2019.11.278
• Subjects: ZIRCÔNIA; PORCELANA DENTÁRIA
• Agências de fomento:
  • Financiamento FAPERJ
  • Financiamento CNPq
• Language: Inglês
• Abstract: The effects of different surface finishing procedures on the translucency of yttria stabilized zirconia ceramics (ZrO2) were evaluated. ZrO2-3mol.%Y2O3 (designed Zr3) or ZrO2-5mol.%Y2O3(Zr5) specimens with thickness varying between 0.5 and 1.5 mm were obtained by sintering at 1500 °C for 2 h. Surface finishing of the sintered specimens was done in three distinct manners: polishing with diamond pastes, blasting with Al2O3 particles and blasting with Al2O3–SiO2 particles, according to the preparation protocol for dental prostheses. These sample groups were characterized by X-Ray diffraction analysis, scanning electron microscopy, surface roughness and spectrophotometry. The sintered ceramics exhibited relative densities higher than 99% and were composed of 68.5% and 31.5%of tetragonal (t)-ZrO2 and cubic(c)-ZrO2 for composition Zr3 and 25.2% and 74.8% for composition Zr5, respectively. Furthermore, 1.5 to 1.8% of monoclinic (m)-ZrO2, has been found in the blasted surfaces. The average grain size varied from 0.5 μm for Zr3 to 1.45 μm for the Zr5 samples. After polishing, all samples presented a surface roughness Raof about 0.05 μm, while blasting resulted in an increased roughness ranging between 1.24 μm and 1.49 μm.Samples rich in (c)-ZrO2 phase (Zr5) are more translucent than samples rich in (t)-ZrO2 (Zr3) because of their larger grain size and because the cubic phase is less anisotropic than (t)-ZrO2. Furthermore, the translucency of thinner samples is more affected by abrasive blasting because they also present the highly anisotropic monoclinic(m)-ZrO2 phase and, therefore, the reduction of translucency is more pronounced. Parameters such as grain size, crystalline phase composition, porosity and grain boundary density are used to explain the phenomena involved in the differences of translucency of these materials.
• Source:
  • Título: Ceramics international
  • ISSN: 02728842
  • Volume/Número/Paginação/Ano: v., n. , p.7748-7755, 2020

Informações sobre o DOI: 10.1016/j.ceramint.2019.11.278 (Fonte: oaDOI API)
• Este periódico é de assinatura
• Este artigo NÃO é de acesso aberto
  
• Cor do Acesso Aberto: closed

---

How to cite

A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas

• ABNT

  SANTOS, Claudinei dos et al. Effect of surface finishing and thickness on the translucency of zirconia dental ceramis. Ceramics international, n. , p. 7748-7755, 2020Tradução . . Disponível em: https://doi.org/10.1016/j.ceramint.2019.11.278. Acesso em: 29 dez. 2025.

• APA

  SANTOS, C. dos, Rosa, G. O., Quintino, M. N., Alves, M. F. R. P., RIBEIRO, S., & Silva, C. L. M. (2020). Effect of surface finishing and thickness on the translucency of zirconia dental ceramis. Ceramics international, ( ), 7748-7755. doi:10.1016/j.ceramint.2019.11.278

• NLM

  SANTOS C dos, Rosa GO, Quintino MN, Alves MFRP, RIBEIRO S, Silva CLM. Effect of surface finishing and thickness on the translucency of zirconia dental ceramis [Internet]. Ceramics international. 2020 ;( ): 7748-7755.[citado 2025 dez. 29 ] Available from: https://doi.org/10.1016/j.ceramint.2019.11.278

• Vancouver

  SANTOS C dos, Rosa GO, Quintino MN, Alves MFRP, RIBEIRO S, Silva CLM. Effect of surface finishing and thickness on the translucency of zirconia dental ceramis [Internet]. Ceramics international. 2020 ;( ): 7748-7755.[citado 2025 dez. 29 ] Available from: https://doi.org/10.1016/j.ceramint.2019.11.278

Últimas obras dos mesmos autores vinculados com a USP cadastradas na BDPI:

• Effect of Fe2O3 Addition and Sintering Temperature on mechanical Properties and Translucence of Zirconia Dental Ceramics with Different Y2O3 Content
• Zircônia estabilizada com ítria para aplicações odontológicas: propriedades ópticas e mecânicas
• PROPRIEDADES ÓPTICAS E MECÂNICAS DE ZrO2 ESTABILIZADA COM DIFERENTES TEORES DE Y2O3
• Influência da adição do pó da casca de ovo calcinada na resistência à compressão de argamassas 1:3
• Estudo do empacotamento do concreto civil com incorporação de cacos de vidro como agregado graúdo
• The wettability at high temperatures in the technological development of materials
• Effect of niobium addition in support catalysts applied in satellite propulsion
• Evaluation of mechanical properties of porous alumina ceramics obtained using rice husk as a porogenic agent
• Influência da distribuição granulométrica no tempo de secagem e na porosidade de uma cerâmica refratária monolítica
• Comparison of the indentation strength and single-edge-v-notched beam methods for dental ceramic fracture toughness testing