Evaluation of CTOD resistance curves in clamped SE(T) specimens with weld centerline cracks (2020)
- Authors:
- USP affiliated authors: RUGGIERI, CLAUDIO - EP ; AFZALIMIR, SEYED HAMIDREZA - EP ; BARBOSA, VITOR SCARABELI - EP
- Unidade: EP
- DOI: 10.1016/j.engfracmech.2020.107326
- Subjects: MECÂNICA DA FRATURA; FADIGA DOS MATERIAIS; DEFORMAÇÃO E ESTRESSES
- Language: Inglês
- Imprenta:
- Publisher place: Kidlington
- Date published: 2020
- Source:
- Título: Engineering Fracture Mechanics
- ISSN: 0013-7944
- Volume/Número/Paginação/Ano: v. 195, p. 297-312, maio 2018
- Status:
- Artigo possui versão em acesso aberto em repositório (Green Open Access)
- Versão do Documento:
- Versão submetida (Pré-print)
- Acessar versão aberta:
-
ABNT
AFZALIMIR, Seyed Hamidreza e BARBOSA, Vitor Scarabeli e RUGGIERI, Claudio. Evaluation of CTOD resistance curves in clamped SE(T) specimens with weld centerline cracks. Engineering Fracture Mechanics, v. 195, p. 297-312, 2020Tradução . . Disponível em: https://doi.org/10.1016/j.engfracmech.2020.107326. Acesso em: 06 maio 2026. -
APA
Afzalimir, S. H., Barbosa, V. S., & Ruggieri, C. (2020). Evaluation of CTOD resistance curves in clamped SE(T) specimens with weld centerline cracks. Engineering Fracture Mechanics, 195, 297-312. doi:10.1016/j.engfracmech.2020.107326 -
NLM
Afzalimir SH, Barbosa VS, Ruggieri C. Evaluation of CTOD resistance curves in clamped SE(T) specimens with weld centerline cracks [Internet]. Engineering Fracture Mechanics. 2020 ; 195 297-312.[citado 2026 maio 06 ] Available from: https://doi.org/10.1016/j.engfracmech.2020.107326 -
Vancouver
Afzalimir SH, Barbosa VS, Ruggieri C. Evaluation of CTOD resistance curves in clamped SE(T) specimens with weld centerline cracks [Internet]. Engineering Fracture Mechanics. 2020 ; 195 297-312.[citado 2026 maio 06 ] Available from: https://doi.org/10.1016/j.engfracmech.2020.107326 - Towards the prediction of hydrogen–induced crack growth in high–graded strength steels
- Effects of increased span on fracture toughness using non-standard PCVN specimens and implications for the reference temperature, T0
- Fracture toughness testing using non-standard bend specimens – Part II: Experiments and evaluation T0 reference temperature for a low alloy structural steel
- Fracture toughness testing using non-standard bend specimens – Part I: Constraint effects and development of test procedure
- A simplified estimation procedure for the Weibull stress parameter, m, and applications to predict the specimen geometry dependence of cleavage fracture toughness
- Temperature dependence of cleavage fracture toughness for an ultrahigh strength martensitic steel
- Investigation of the inverse fracture occurrence in X65 Q&T pipeline steels under impact loading: Part I: Experiments
- Exploratory experimental evaluation of crack growth resistance properties for a nickel-chromium girth weld of a clad lined pipe
- Ductile fracture resistance measurements in a nickel-chromium girth weld of a Clad line pipe
- Investigação experimental dos efeitos de geometria e de carregamento sobre a distribuição dos valores de tenacidade à fratura por clivagem medidos na região de transição dúctil-frágil de um aço estrutural ferrítico
Informações sobre a disponibilidade de versões do artigo em acesso aberto coletadas automaticamente via oaDOI API (Unpaywall).
Por se tratar de integração com serviço externo, podem existir diferentes versões do trabalho (como preprints ou postprints), que podem diferir da versão publicada.
Download do texto completo
| Tipo | Nome | Link | |
|---|---|---|---|
 |
Ruggieri-2020-Evaluation ... | Direct link |
How to cite
A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas