Failure analysis of impact-damaged / hydrothermally aged fiber-reinforced polymer matrix composite joints subjected to blend loading (2014)
- Authors:
- Autor USP: TARPANI, JOSÉ RICARDO - EESC
- Unidade: EESC
- Subjects: POLÍMEROS (MATERIAIS); MECÂNICA DA FRATURA; FALHA
- Language: Inglês
- Imprenta:
- Publisher: European Society for Composite Materials - ESCM
- Publisher place: Patras
- Date published: 2014
- Source:
- Título do periódico: Proceedings
- Conference titles: European Conference on Composite Materials - ECCM16
-
ABNT
TARPANI, José Ricardo et al. Failure analysis of impact-damaged / hydrothermally aged fiber-reinforced polymer matrix composite joints subjected to blend loading. 2014, Anais.. Patras: European Society for Composite Materials - ESCM, 2014. . Acesso em: 20 mar. 2023. -
APA
Tarpani, J. R., Castro, C. E. G., Pickering, S. G., Almond, D. P., & Amico, S. C. (2014). Failure analysis of impact-damaged / hydrothermally aged fiber-reinforced polymer matrix composite joints subjected to blend loading. In Proceedings. Patras: European Society for Composite Materials - ESCM. -
NLM
Tarpani JR, Castro CEG, Pickering SG, Almond DP, Amico SC. Failure analysis of impact-damaged / hydrothermally aged fiber-reinforced polymer matrix composite joints subjected to blend loading. Proceedings. 2014 ;[citado 2023 mar. 20 ] -
Vancouver
Tarpani JR, Castro CEG, Pickering SG, Almond DP, Amico SC. Failure analysis of impact-damaged / hydrothermally aged fiber-reinforced polymer matrix composite joints subjected to blend loading. Proceedings. 2014 ;[citado 2023 mar. 20 ] - Fadiga após múltiplos impactos em laminados carbono-epóxi
- Nondestructive testing with thermography
- Tenacidade à fratura translaminar dinâmica de um laminado híbrido metal-fibra para uso em elevadas temperaturas
- Digital versus conventional radiography for imaging fatigue cracks in riveted lap joints of hybrid glass reinforced fiber/metal laminate
- Magnetic resonance imaging of contaminated and damaged core cells in polymer composite sandwich panels
- Tenacidade à fratura translaminar dinâmica de um laminado híbrido fibra-metal carbono-titânio de grau aeronáutico
- Fadiga de baixo ciclo em material híbrido fibra-metal Glare-5
- USP poderá firmar parceria de US
- Radiografia direta aplicada à monitoração de trincas de fadiga em juntas mistas de Glare ensaiadas em ambiente salino
- Inspeção termográfica de danos por impacto em laminados compósitos estruturais sólidos de matriz polimérica
How to cite
A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas