Intergranular corrosion in a martensitic stainless steel detected by electrochemical tests (1999)
- Authors:
- USP affiliated authors: FALLEIROS, NEUSA ALONSO - EP ; FALLEIROS, IVAN GILBERTO SANDOVAL - EP
- Unidade: EP
- Subjects: CORROSÃO; ELETROQUÍMICA; AÇO INOXIDÁVEL
- Language: Inglês
- Abstract: Quenched and tempered martensitic stainless steel UNS S41000 was tested electrochemically for susceptibility to sensitization in specimens quenched from 975ºC (1,248 K) and tempered for 2 h at different temperatures between 300ºC (573 K) and700ºC(973 K). Besides an oxalic acid etch test, the following tests were performed using a potentiostat and 1 N sulfuric acid (H2SO4) solution: potentiokinetic polarization, potentiostatic etch, and electrochemical potentiokinetic reactivationin thedouble-loop version (DL-EPR). Tested surfaces were observed metallographically. The maximum susceptibility to intergranular corrosion was observed in the condition tempered at 550ºC (823 K), and a sensitized structure was detected. Forlowertempering temperatures, steel was less sensitized, or not at all, and for higher tempering temperatures, steel was less sensitized. All tests except for the oxalic acid etch were able to evaluate quantitatively different degress ofsensitizationas a function of tempering temperature. The DL-EPR method was the best to discriminate degrees of sensitization
- Imprenta:
- Source:
-
ABNT
ALONSO-FALLEIROS, Neusa e MAGRI, Marcelo e FALLEIROS, Ivan Gilberto Sandoval. Intergranular corrosion in a martensitic stainless steel detected by electrochemical tests. Corrosion, v. 55, n. 8, p. 769-778, 1999Tradução . . Acesso em: 27 jan. 2026. -
APA
Alonso-Falleiros, N., Magri, M., & Falleiros, I. G. S. (1999). Intergranular corrosion in a martensitic stainless steel detected by electrochemical tests. Corrosion, 55( 8), 769-778. -
NLM
Alonso-Falleiros N, Magri M, Falleiros IGS. Intergranular corrosion in a martensitic stainless steel detected by electrochemical tests. Corrosion. 1999 ; 55( 8): 769-778.[citado 2026 jan. 27 ] -
Vancouver
Alonso-Falleiros N, Magri M, Falleiros IGS. Intergranular corrosion in a martensitic stainless steel detected by electrochemical tests. Corrosion. 1999 ; 55( 8): 769-778.[citado 2026 jan. 27 ] - Transformações estruturais durante a homogeneização de alumínio comercialmente puro
- Microestruturas de um latão alfa-beta resultantes de encruamento e recozimento
- Austenitização de um aço hipoeutetóide a partir do estado esferoidizado e do estado normalizado
- Bases para o futuro [ Entrevista a Juliana Nakamura]
- Resultados obtidos com a substituicao de ferro fundido cinzento por nodular em lingoteiras
- Materiais , processos, solicitacoes ou mercados avancados?
- Efeito da microssegregacao e de tratamentos de recozimento na microestrutura do aco aisi 52100 apos tempera
- Efeito da microestrutura previa nas temperaturas de formacao da austenita e na cinetica das transformacoes isotermicas do aco aisi 52100
- Efeito da microssegregacao e de tratamentos de recozimento na microestrutura do aco aisi 52100 apos tempera
- Efeito de um tratamento termico de homogeneizacao na resistencia ao impacto do aco maraging-18% niquel, grau 1990 mpa
How to cite
A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas