Characterization of a New Fe-C-Mn-Si-Cr Bearing Alloy: Tempered Martensite Embrittlement Susceptibility (2014)
- Authors:
- USP affiliated authors: GOLDENSTEIN, HELIO - EP ; MARCOMINI, JOSÉ BENEDITO - EEL
- Unidades: EP; EEL
- DOI: 10.1007/s11665-013-0800-z
- Subjects: LIGAS METÁLICAS; AÇO
- Language: Inglês
- Imprenta:
- Source:
- Título do periódico: Journal of Materials Engineering and Performance
- ISSN: 1059-9495
- Volume/Número/Paginação/Ano: v. 23, n.3, p. 780-785, 2014
- Este periódico é de assinatura
- Este artigo NÃO é de acesso aberto
- Cor do Acesso Aberto: closed
-
ABNT
MARCOMINI, José Benedito e GOLDENSTEIN, Hélio. Characterization of a New Fe-C-Mn-Si-Cr Bearing Alloy: Tempered Martensite Embrittlement Susceptibility. Journal of Materials Engineering and Performance, v. 23, n. 3, p. 780-785, 2014Tradução . . Disponível em: https://doi.org/10.1007/s11665-013-0800-z. Acesso em: 19 abr. 2024. -
APA
Marcomini, J. B., & Goldenstein, H. (2014). Characterization of a New Fe-C-Mn-Si-Cr Bearing Alloy: Tempered Martensite Embrittlement Susceptibility. Journal of Materials Engineering and Performance, 23( 3), 780-785. doi:10.1007/s11665-013-0800-z -
NLM
Marcomini JB, Goldenstein H. Characterization of a New Fe-C-Mn-Si-Cr Bearing Alloy: Tempered Martensite Embrittlement Susceptibility [Internet]. Journal of Materials Engineering and Performance. 2014 ; 23( 3): 780-785.[citado 2024 abr. 19 ] Available from: https://doi.org/10.1007/s11665-013-0800-z -
Vancouver
Marcomini JB, Goldenstein H. Characterization of a New Fe-C-Mn-Si-Cr Bearing Alloy: Tempered Martensite Embrittlement Susceptibility [Internet]. Journal of Materials Engineering and Performance. 2014 ; 23( 3): 780-785.[citado 2024 abr. 19 ] Available from: https://doi.org/10.1007/s11665-013-0800-z - Caracterização da nova liga Fe-C-Mn-Si-Cr: fragilização da martensita revenida e curvas de revenimento
- Stress corrosion cracking and fatigue crack growth of an API 5L X70 welded joint in an ethanol environment
- Stress corrosion cracking and corrosion fatigue analysis of API X70 steel exposed to a circulating ethanol environment
- Influência do etanol sobre o comportamento em fadiga do aço API 5L X70
- Austenite grain refinement of alloyed ductile iron
- Classification and characterisation of 'infinito'-M2C and 'infinito'-MC eutectics in M2 high speed steel
- Infiltration-diffusional-solidification (IDS) A P/M+liquid metal infiltration route for processing metal matrix composites
- Effect of modification treatment on microporosity formation in 356 Al alloy
- Producao e caracterizacao de materiais compositos de matriz metalica Al/Sic obtidos por extrusao de pós
- Reactions between steel wires and molten 'ZN'-'AL' alloys
Informações sobre o DOI: 10.1007/s11665-013-0800-z (Fonte: oaDOI API)
How to cite
A citação é gerada automaticamente e pode não estar totalmente de acordo com as normas